Quantitative structural characterization of the melting behavior of isotactic polypropylene†
Hercules Research Center Contribution No. 1629.
Abstract
The melting behavior of restrained isotactic polypropylene fibers is examined quantitatively in terms of the influence the anisotropic structural state of the polymer has on the observed properties. Two endotherm peaks are observed to occur in some of the samples. The formation and location of the multiple peaks are determined by the orientation of the noncrystalline chains, and is independent of the fabrication path used to achieve that orientation. Above a certain minimum orientation of the noncrystalline chains, multiple endotherm peak formation occurs. The high-temperature endotherm (T2M) extrapolates to an ultimate melting point for fully oriented noncrystalline chains of 220°C, while the lower-temperature endotherm (T1M) extrapolates to an ultimate melting point of 185°C. Noncrystalline chain orientation influences the endotherm temperature through its changing configurational entropy. It is shown quantitatively that the noncrystalline polymer must be considered as plastically deformed, since rubber elasticity theory is not followed as predicted. The melting behavior of isothermally crystallized samples are also reported to further elucidate the nature of the observed endotherms.